A K , Jha and T K, Dan and S V , Prasad and P K , Rohtagi (1986) Al alloy-solid lubricant talc particle composites. Journal of Materials Science, 21. pp. 3681-3685. ISSN 0022-2461

Full text not available from this repository. (Request a copy)

Abstract

This paper describes the method of synthesizing cast aluminium alloy talc particulate composites and their mechanical and wear properties. Talc particles were characterized using X-ray diffraction, infrared spectroscopy and differential thermal analysis techniques. Composites with two Al-Si alloys (LM 13 and LM 6) as matrices were prepared by heating the molten alloys to 750° C and adding the preheated talc powder (−150 + 50 μm size) after creating a vortex by mechanically stirring the melt. Simultaneous addition of 2 wt% Mg was found to facilitate the introduction and dispersion of talc particles in molten Al-Si alloys. Composites containing 2.8 wt % talc in LM 13 and 2 wt % talc in LM 6 have been prepared. Optical micrographs of composites revealed uniform distribution of talc particles. Hardness and tensile strength of LM 13+2.8% talc were 85 BHN and 126 MPa, respectively. After suitable heat treatment hardness and strength were increased to 125 BHN and 211 MPa respectively. Wear rates of LM 13+2.8 wt% talc and LM 6+2 wt % talc composites were found to be 22 to 30% less than the wear rates of corresponding base alloys without any dispersions.

Item Type:	Article
Subjects:	Lightweight Materials > Metal Matrix Composites
Divisions:	UNSPECIFIED
Depositing User:	Mr. B.K. Prasad
Date Deposited:	13 Aug 2013 11:56
Last Modified:	05 Mar 2014 07:29
URI:	http://ampri.csircentral.net/id/eprint/342

Actions (login required)

View Item