Singh, I.B. and Chaturvedi, K and Dr., A H Yegneshwaran (2007) Thermal Immobilization of Cr, Cu and Zn of Galvanizing Waste in the Presence of Clay and Fly Ash. Environment and Technology.

Full text not available from this repository. (Request a copy)

Abstract

In the present investigation thermal treatment of galvanizing waste with clay and fly ash has been carried out to immobilize Cr, Zn, Cu and other metals of the waste at temperature range 850 degrees C to 950 degrees C. Leaching of the metals from the waste and solidified product was analyzed using toxic characteristic leaching procedure (TCLP). Results indicated that the composition of waste and clay treatment temperature are the key factors in determining the stability of solidified product. After heating at 950 degrees C, the solidified specimens of 10% waste with clay have shown comparatively a high compressive strength and less water absorption. However, a decrease in compressive strength and increase in water absorption were noticed after addition of 15% of waste with clay. The leachability of all the metals present in the waste was found to reduce considerably with the increase of treatment temperature. In the case of Cr and Zn, their leachabilty was found at unacceptable levels from the treated product obtained after heating at 850 degrees C However, their leachability was reduced significantly within an acceptable level after treatment at 950 degrees C. The thermal treatment has shown an increase of re-oxidation trend of Cr (III) to Cr (VI) up to 900 degrees C of heating and this trend became almost zero after heating at 950 degrees C. Addition of fly ash did not show any improvement in strength, durability and leachability of metals from the thermally treated product. X-ray diffraction (XRD) analysis of the product confirmed the presence of mixed phases of oxides of toxic metals.

Item Type:	Article
Subjects:	CSIR-800 > Environmental Studies/Chemistry Waste-to-Wealth
Divisions:	UNSPECIFIED
Depositing User:	Mr. B.K. Prasad
Date Deposited:	13 Jan 2014 08:16
Last Modified:	27 Feb 2014 07:21
URI:	http://ampri.csircentral.net/id/eprint/967

Actions (login required)

View Item